steel cut wire shot
provide
1.0mm 1.2mm 1.5mm
45-55HRC
competitve
polished bright
blasting, cleaning
Ton
5
Shanghai
10-15days
25kgs/bag,1000kgs/ton bag
Yes
500 / Year
L/C, T/T, Western Union
Steel cut wire shot
Good price Steel wire cut shot ( recycled material)
are Mostly used in blasting,shot blasting and shot peening,Casting, Mechanical,
Casting,Shipbuilding, Automotive, Container, Steel and other industries.
Used in blast room, blast machine, blast gun and so on
Specifications
Recycled / old steel wire cut shot, and cost are lower, surface is polished and clean!
Steel cut wire shot used for welding ,blasting, coating, cleaning products.
|
Name |
steel cut wire shot Recycled steel wire cut shot |
|
|
Chemistry |
(C) |
0.45~0.75% |
|
(Mn) |
0.4~1.20% |
|
|
(Si) |
0.10~0.30% |
|
|
(S) |
≤0.04% |
|
|
(P) |
≤0.04% |
|
|
Average Hardness |
41~45HRC 45-50HRC 50-55HRC |
|
|
Hardness |
±3.0HRC(±40HV) |
|
|
Tensile Strength |
1660-2200Mpa |
|
|
Density |
7.4g/cm3 |
|
|
size |
1.0,1.5,1.8,2.0,2.5mm |
|
|
SAE |
CW0.9,1.0,1.4,1.5,1.8,2.0 |
|
Usage/Application
Blast cleaning: cleaning of casting, die-casting, forging;
Sand removal :casting, steel plate, H type steel, steel structure.
Shot peening: gear, heat treated parts.
Rust removal: Rust removal of casting, forging, steel plate, H type steel, steel structure.
Shot blasting: profile steel, ship board, steel board, steel material,steel structure.
Pre-treatment: metal surface, steel board, profile steel, steel structure, before painting or coating.
Package:
1. 25kg /bag, 1000kgs/ 40bags in a ton bag.
2. or 1000kgs in ton bag
3. Package according to customer requirement.
Mareks:1*20 container, 22-26 metric tons/ container.
Best supplier of steel cut wire shot, could be conditioned to round balls.
Honest supplier, You can trust on us!!!
Delivery fast, Maintain good quality, Competitive price
Welcome contact with me, Will reply to you soon.