ll Products Description
Chrome alloyed casting grinding steel ball (Dia.20-150mm) is widely used in cement building materials, metal mines, and other industries for powder preparation and superfine processing. The hardness reaches 45-65HRC, and the distribution of the hardness gradient is average. The property- low abrasion, good toughness and less breakage, prolongs its life, improves the productivity of the ball mill, and lowers the cost. Our quality is accord with GB/T17445-2009 standard.
Processing Technique
Intermediate frequency furnace smelting high-quality steel scrap and chromium alloy etc.
Constant temperature casting process ensuring the quality, no sonim, no pore, no mal-roundness etc.
Oil-immersed heat treatment and annealing process changing the internal organizational structure, lowering the breakage, and improving the performance.
Matter test, after the furnace test, semi-finished products and end products inspection was done by advanced spectrometer and durometer imported from Germany.
Chemical Elements
Name |
Chemical Elements (%) |
|||||||
C |
Si |
Mn |
Cr |
Mo |
Cu |
P |
S |
|
Low Cr Balls |
2.1-3.6 |
≤1.5 |
0.3-1.5 |
0.8-1.8 |
≤0.8 |
≤1.0 |
≤0.06 |
≤0.06 |
Medium Cr Balls |
2.1-3.3 |
≤1.5 |
0.3-1.5 |
3-6 |
≤0.8 |
≤1.0 |
≤0.06 |
≤0.06 |
High Cr Balls |
2.0-3.3 |
≤1.2 |
0.3-1.5 |
10-13 |
≤0.8 |
≤0.6 |
≤0.06 |
≤0.06 |
Special High Cr |
2.0-3.3 |
≤1.2 |
0.3-1.5 |
15-23 |
≤0.8 |
≤0.6 |
≤0.06 |
≤0.06 |
Physical Property & Microstructure
Name |
HRC |
Ak(J/cm2) |
Microstructure |
Times of Falling Balls |
|
Low Cr Balls |
≥45 |
≥2.5 |
P+C |
≥10000 |
|
Medium Cr Balls |
≥48 |
≥3.0 |
P+C |
≤Φ80 |
≥15000 |
≥Φ80 |
≥10000 |
||||
High Cr Balls |
≥58 |
≥4 |
M+C+A |
≤Φ80 |
≥15000 |
≥Φ80 |
≥10000 |
||||
M-Martensite P-Pearliet C-Carbide A-Austenite |
Size & Weight
Size(mm) |
Weight(kg/pc) |
Quantity(pc/t) |
Size(mm) |
Weight(kg/pc) |
Quantity(pc/t) |
|
Φ30 |
0.11 |
9091 |
Φ90 |
2.90 |
345 |
|
Φ40 |
0.25 |
3891 |
Φ100 |
4.00 |
250 |
|
Φ50 |
0.50 |
2000 |
Φ110 |
5.30 |
188 |
|
Φ60 |
0.86 |
1153 |
Φ120 |
6.80 |
147 |
|
Φ70 |
1.37 |
729 |
Φ130 |
7.70 |
129 |
|
Φ80 |
2.05 |
487 |
Φ140 |
8.74 |
114 |
Why choosing H&G grinding steel ball
1. Over 20years Professional casting grinding balls manufacturing experience, deserves your trust.
2. High quality, competitive price and good service benefit our customers.
3. ISO9001 certified company, advanced oil quenching and heating production line, together with advanced testing machines imported from Germany are used to ensure the quality.
4. Chemical analysis reports would be sent together with each batch of steel balls, even samples.
5. Skilled sales & service team in Shanghai branch can provide timely good service.
6. 200 thousand Tons annual production capacity can provide short L/T.