Materials: SUS304/SUS41/SUS430 Stainless steel wire
Shape: Spherical (Conditioned) and Cylinder (As cut)
Size: 0.2mm-2.5mm, for customization
Durability:6500 Times
MOQ: 25kgs
Sample free
Certificate:ISO9001:2008,GB/T470-1997
Standards: AMS 2431, MIL-S-13165C, DIN8201, VDFI8001, SAEJ827, SAEJ441
Usage: shot blasting;shot peening;surface cleaning, rust remove,surface treatmentAdvantages: Uniform size;Uniform Hardness;Small Dust.any query please feel free let me know by info(at)sunhaw(dot)cn
Main technical indicators of stainless steel shot:
|
Products |
Stainless Steel Shot |
Stainless Steel Cut Wire Shot |
|
Shape |
Conditioned (Spherical) |
As cut (Cylindrical) |
|
Sizes specifications |
From 0.2mm to 2.5mm |
|
|
Standards |
In accordance with AMS 2431, MIL-S-13165C, DIN8201, VDFI8001, SAEJ827, SAEJ441 standards |
|
|
Chemical composition 304Type |
Carbon (C) |
≤0.12% |
|
Manganese (Mn) |
≤2.00% |
|
|
Silicon (Si) |
≤1.00% |
|
|
Chromium (Cr) |
17~19% |
|
|
Nickel (Ni) |
7~10% |
|
|
Sulfur (S) |
≤0.03% |
|
|
Phosphorus (P) |
≤0.035% |
|
|
Microhardness |
308～509 HV Vickers 41～59 HRC Rockwell |
|
|
Tensile intension |
490~1520 Mpa |
|
|
Durability |
6500Times (1.0mm, VDFI8001) |
|
|
Microstructure |
Deformed Austenite |
|
|
Density |
7.8 g/cm3 |
|
|
Bulk density |
4.7 g/cm3 |
|
|
Note: Part of the 304 Austenite stainless steel shot will convert into Marten site type, getting magnetic through a process of drawing, cutting and rounding. |
||
ADVANTAGES OF CUT WIRE SHOT:
1. Most economical and lowest consumption.
2. Available in various sizes as per requirement.
3. More life span, till completely reduced to smallest tiny particle.
4. Increases the fatigue life of the blasted components.
5. No possibility for dust formation during shot blasting.
6. Cleans the product faster.
7. Performance Consistency
8. Reduced Time for Shot Blasting/Peening
9. Cuts down the maintenance cost of shot blasting machine.
10. Environment friendly. no dust or health hazard during operation.
11. Uniform cleaning and comparatively brighter surface
12. Raw Material is of exact composition without any material defect (blow holes, porosity, shrinkage etc.),
13. Price advantage over steel shots